BINDERLESS PANELS MADE WITH BLACK SPRUCE BARK

Zhenhua Gao, Xiang-Ming Wang, Hui Wan, Gilles Brunette

Abstract


The bark of black spruce was thermo-mechanically refined and used to manufacture binderless bark-based fiberboard with various pressing temperatures, times, and panel structures in order to utilize an abundant bark resource for a better value-added application. The test results indicated that it is technically feasible to manufacture binderless fiberboard with refined black spruce bark through self-bonding under elevated temperatures over a reasonable period of pressing time. Binderless bark-based fiberboards with a homogeneous structure had very poor flexural properties due to the poor strength of bark itself; however, by using a sandwich structure with 30wt% wood fiber in the surface layers and 70wt% bark in the core layer it was possible to sufficiently improve panel flexural properties so that the manufactured binderless bark-based fiberboards was able to meet the mechanical property requirements of 115-grade fiberboard according to ANSI A208.2 (2009). Refining conditions had a great impact on the mechanical properties of binderless bark-based fiberboard.

Keywords


Bark; Binderless fiberboard; Refining conditions; Mechanical properties

Full Text: PDF

Welcome to BioResources! This online, peer-reviewed journal is devoted to the science and engineering of biomaterials and chemicals from lignocellulosic sources for new end uses and new capabilities. The editors of BioResources would be very happy to assist you during the process of submitting or reviewing articles. Please note that logging in is required in order to submit or review articles. Martin A. Hubbe, (919) 513-3022, hubbe@ncsu.edu; Lucian A. Lucia, (919) 515-7707, lucian.lucia@gmail.com URLs: bioresourcesjournal.com; http://ncsu.edu/bioresources ISSN: 1930-2126