Borate-Treated Strand Board from Southern Wood Species: Resistance Against Decay and Mold Fungi

Xinwu Xu, Sunyoung Lee, Yiqiang Wu, Qinglin Wu

Abstract


Combined decay and mold resistance of zinc borate-(ZB) and calcium borate-(CB) treated oriented strand board (OSB) from southern mixed hardwood (MHW) and southern yellow pine (SYP) was investigated. Tests were done with a brown-rot fungus, Gloeophyllum trabeum, and a white-rot fungus, Trametes versicolor, for 8 and 12 weeks, respectively. Wood species and fungus type had significant influence on the decay resistance. Decay caused by the brown-rot fungus was evident for all untreated SYP and mixed MHW controls. White-rot fungus did not cause significant sample weight loss for either species group. In the SYP OSB control inoculated with G. trabeum, the hyphae were abundant in wood rays and cell walls where they primarily penetrated through bordered and simple pits. The incorporation of ZB and CB into OSB provided significant protection against the fungi with no significant weight loss observed in the treated OSB. Microscopic analysis showed distinct evidence of fungal colonization and a thinning pattern of cell wall material. Untreated OSB samples from MHW and commercial OSBs were most susceptible to mold growth after 6 weeks. The borate-modified OSB from MHW and SYP effectively prevented the mold growth.

Keywords


Zinc borate; Calcium borate; Strandboard; Decay; Mold

Full Text: PDF

Welcome to BioResources! This online, peer-reviewed journal is devoted to the science and engineering of biomaterials and chemicals from lignocellulosic sources for new end uses and new capabilities. The editors of BioResources would be very happy to assist you during the process of submitting or reviewing articles. Please note that logging in is required in order to submit or review articles. Martin A. Hubbe, (919) 513-3022, hubbe@ncsu.edu; Lucian A. Lucia, (919) 515-7707, lucian.lucia@gmail.com URLs: bioresourcesjournal.com; http://ncsu.edu/bioresources ISSN: 1930-2126