Effect of Modification with Phenol Formaldehyde Resin on the Mechanical Properties of Wood from Chinese Fir

Yanhui Huang, Benhua Fei, Yan Yu, Rongjun Zhao

Abstract


Samples of Chinese fir were treated with either low-molecular-weight or commercial phenol-formaldehyde (PF) resins. The macro- and micromechanical properties of the treated and untreated samples were determined. The average longitudinal tensile modulus of elasticity (MOE) was 30.88% larger for the samples treated with the low-molecular-weight PF resin than it was for the untreated samples. The average MOE of the samples treated with the commercial PF resin was 29.84% less than that of the untreated samples. The micromechanical properties of the samples were investigated through nanoindentation studies. For the samples modified with low-molecular-weight PF resin, the values of average MOE and hardness were 32.94 and 32.93%, respectively, greater than those of the untreated samples. In contrast, the average MOE and hardness values were 11.99 and 18.14%, respectively, greater for the samples modified with commercial PF resin compared to the untreated samples. It could be inferred that the low-molecular-weight PF resin was able to diffuse into the nanopores in the S2 layer of the tracheid cell wall of the Chinese fir, thereby improving its macromechanical properties. Modification with low-molecular-weight PF resin was an effective way to enhance the longitudinal macromechanical properties of wood from the Chinese fir.

Keywords


Phenol-formaldehyde resin; Mechanical properties; Cell wall; Modulus of elasticity; Hardness

Full Text: PDF

Welcome to BioResources! This online, peer-reviewed journal is devoted to the science and engineering of biomaterials and chemicals from lignocellulosic sources for new end uses and new capabilities. The editors of BioResources would be very happy to assist you during the process of submitting or reviewing articles. Please note that logging in is required in order to submit or review articles. Martin A. Hubbe, (919) 513-3022, hubbe@ncsu.edu; Lucian A. Lucia, (919) 515-7707, lucian.lucia@gmail.com URLs: bioresourcesjournal.com; http://ncsu.edu/bioresources ISSN: 1930-2126