A Simple Nickel Activation Process for Electroless Nickel-Phosphorus Plating on Carbon Fiber

Tingguo Yan, Leihong Li, Lijuan Wang

Abstract


A new nickel activation process was developed for metalizing the carbon fiber (CF) surface with electroless nickel plating. The oxidation and activation processes were examined using X-ray Photoelectron Spectroscopy (XPS), Scanning Electron Microscopy (SEM), Energy Dispersive X-ray Spectrometry (EDS), and X-ray Diffractometry (XRD). XPS analysis showed that HNO3 oxidation improved the O/C ratio of the CF surface, which resulted in an increase in the amount of oxygen-containing groups. As activation time increased, both Nio cluster and Ni-P deposits increased. More than 50 mg of Nio clusters formed on the surface of 1g CF. SEM observations illustrated that particles and island-like shapes were developed from the Nio cluster, which helped to initiate the electroless nickel-plating on the CF surface. A continuous and compact coating with a thickness of about 2 to 3 μm was obtained. EDS results showed that the nickel and phosphorus content in the deposits was 97.34 wt.% and 2.66 wt.%, respectively. XRD indicated that the Ni-P coating was crystalline and the maximum deposition on 1 g CFs was as high as 9000 mg. As the results of the observations reveal, the activation method is a feasible alternative to Pd activation.

Keywords


Electroless nickel plating; Carbon fiber (CF); Ni activation; Coating

Full Text: PDF

Welcome to BioResources! This online, peer-reviewed journal is devoted to the science and engineering of biomaterials and chemicals from lignocellulosic sources for new end uses and new capabilities. The editors of BioResources would be very happy to assist you during the process of submitting or reviewing articles. Please note that logging in is required in order to submit or review articles. Martin A. Hubbe, (919) 513-3022, hubbe@ncsu.edu; Lucian A. Lucia, (919) 515-7707, lucian.lucia@gmail.com URLs: bioresourcesjournal.com; http://ncsu.edu/bioresources ISSN: 1930-2126