Investigation of Low Mole Ratio UF and UMF Resins Aimed at Lowering the Formaldehyde Emission Potential of Wood Composite Boards

An Mao, El Barbary Hassan, Moon G. Kim

Abstract


Urea-melamine-formaldehyde (UMF) resins with 2.5% and 5.0% melamine levels added at the beginning of the third step of the typical urea-formaldehyde (UF) synthesis procedure were synthesized with an F/(U+M) mole ratio of 1.05 and evaluated as particleboard binders to investigate the positive effects of melamine on the formaldehyde content and physical performance of boards. Resins were tested for storage properties and analyzed by 13C NMR. Curing catalysts were studied, curing rates were measured, and laboratory particleboards were prepared and tested for formaldehyde contents as well as strength and water-soak test values. The UMF resins resulted in slower curing rates but had adequate board strength values. The formaldehyde content values were within the newly created California emission law (5.2 to 8.0 mg/100 g board). Another objective of this work was to establish the baseline performance of these resins for use in subsequent studies that will aim to reveal the effects of methylene-ether group contents on formaldehyde emissions.

Keywords


Urea-formaldehyde; Urea-melamine-formaldehyde; Particleboards

Full Text: PDF

Welcome to BioResources! This online, peer-reviewed journal is devoted to the science and engineering of biomaterials and chemicals from lignocellulosic sources for new end uses and new capabilities. The editors of BioResources would be very happy to assist you during the process of submitting or reviewing articles. Please note that logging in is required in order to submit or review articles. Martin A. Hubbe, (919) 513-3022, hubbe@ncsu.edu; Lucian A. Lucia, (919) 515-7707, lucian.lucia@gmail.com URLs: bioresourcesjournal.com; http://ncsu.edu/bioresources ISSN: 1930-2126