Preparation and Characterization of Nano-TiO2 Loaded Bamboo-based Activated Carbon Fibers by H2O Activation

Dongna Li, Xiaojun Ma, Xinyan Liu, Lili Yu


As the support for loading TiO2, bamboo-based activated carbon fibers (BACFs) were obtained from Phyllostachys pubescens Mazel after liquefaction using phenol, melt-spinning, curing carbonization, and H2O activation. TiO2/BACFs were prepared by the sol–gel method and characterized by SEM, XRD, FTIR, and XPS. Anatase TiO2 film with high photocatalytic activity was formed on the surface of BACFs, and the average crystallite size of the TiO2 film was 17 to 30 nm. The characteristic absorbance peaks of anatase TiO2 were observed at 1402 and 541 to 605 cm-1 on the infrared spectrum of TiO2/BACFs. The surface of TiO2/BACFs was mainly comprised of C–C, C–O, C=O, and Ti-O bonds. With increased calcination temperature, the contents of element Ti and Ti-O bonds of lattice oxygen on the surface of TiO2/BACFs increased and then decreased. The degradation rate of TiO2/BACFs for methylene blue (MB) solution reached more than 98% after 7 h of UV illumination.


Bamboo-based activated carbon fibers; Nano-TiO2; Loaded; Photocatalyst; Characterization

Full Text: PDF

Welcome to BioResources! This online, peer-reviewed journal is devoted to the science and engineering of biomaterials and chemicals from lignocellulosic sources for new end uses and new capabilities. The editors of BioResources would be very happy to assist you during the process of submitting or reviewing articles. Please note that logging in is required in order to submit or review articles. Martin A. Hubbe, (919) 513-3022,; Lucian A. Lucia, (919) 515-7707, URLs:; ISSN: 1930-2126