The Preparation of Cellulose/Collagen Composite Films using 1-Ethyl-3-Methylimidazolium Acetate as a Solvent

Min Zhang, Cuicui Ding, Lihui Chen, Liulian Huang


Cellulose/collagen composite films with weight ratios of 30/1 (Blend-1) and 10/1 (Blend-2) were prepared using 1-ethyl-3-methylimidazolium acetate as a common solvent. The morphology of the films observed with a field-emission scanning electron microscope displayed a dependence on the ratio of cellulose/collagen. Collagen was successfully composited with cellulose without degradation and showed a denaturation temperature (Td) higher than that of native collagen. Fourier transform infrared spectroscopy suggested that there were hydrogen-bond interactions between collagen and cellulose in the regenerated composite films. Thermogravimetric analysis revealed that the maximum decomposition temperature (Tmax) of cellulose decreased after regeneration, while the Tmax of Blend-1 increased; however, it was reduced again for Blend-2. Elastic moduli from dynamic mechanical analysis exhibited a trend similar to that of Tmax. As indicated by X-ray diffraction, the distance between cellulose molecular chains was shortened for Blend-1 and elongated for Blend-2. Furthermore, the crystallization indices were calculated to be 75.3%, 68.3%, 66.2%, and 55.4% for native cellulose, regenerated films of cellulose, Blend-1, and Blend-2, respectively. These results confirm the dependence of the structural properties of composite films on cellulose/collagen ratios through the interactions between cellulose and collagen.


Cellulose; Collagen; Ionic liquid; Blend

Full Text: PDF

Welcome to BioResources! This online, peer-reviewed journal is devoted to the science and engineering of biomaterials and chemicals from lignocellulosic sources for new end uses and new capabilities. The editors of BioResources would be very happy to assist you during the process of submitting or reviewing articles. Please note that logging in is required in order to submit or review articles. Martin A. Hubbe, (919) 513-3022,; Lucian A. Lucia, (919) 515-7707, URLs:; ISSN: 1930-2126