Preparation of Sugarcane Bagasse/Poly(Acrylic Acid-co-Acrylamide) Hydrogels and their Application

Junli Ren, Weiqing Kong, Runcang Sun

Abstract


In this work, sugarcane bagasse, being an abundant and renewable resource, was used as a raw material to prepare sugarcane bagasse-g-poly(acrylic acid-co-acrylamide) (SB/P(AA-co-AM)) hydrogels. The hydrogels were prepared by free radical graft copolymerization of SB with AA and AM using N,N-methylene-bis-acrylamide (MBA) as a crosslinker. The optimal synthesis conditions were determined by investigating the water absorbency of the hydrogels. The maximum water absorbency reached 269 g/g in deionized water, and the corresponding copper ions adsorption capacity was 265 mg/g. These grafted hydrogels showed a pH-sensitive swelling behavior. Furthermore, they also exhibited excellent water retention capacity, which reserved 92.7%, 81.7%, and 76.8% for 44 h, and 83.7%, 58.6%, and 47.1% for 116 h at 5 °C, 25 °C, and 35 °C, respectively. FTIR spectroscopy and SEM were used to reveal the chemical structure and the morphology of the hydrogels. SEM/EDS further confirmed the adsorption of the copper(II) on the resulting hydrogels. Therefore, SB/P(AA-co-AM) hydrogels could have promising applications as water retention agents and metal ions adsorbents in water treatment and agricultural industries.

Keywords


Sugarcane bagasse; pH-sensitive hydrogels; Water absorbency; Metal ions adsorption; Water retention capacity

Full Text: PDF

Welcome to BioResources! This online, peer-reviewed journal is devoted to the science and engineering of biomaterials and chemicals from lignocellulosic sources for new end uses and new capabilities. The editors of BioResources would be very happy to assist you during the process of submitting or reviewing articles. Please note that logging in is required in order to submit or review articles. Martin A. Hubbe, (919) 513-3022, hubbe@ncsu.edu; Lucian A. Lucia, (919) 515-7707, lucian.lucia@gmail.com URLs: bioresourcesjournal.com; http://ncsu.edu/bioresources ISSN: 1930-2126