Preparation and Characterization of Ammonium Polyphosphate/Diatomite Composite Fillers and Assessment of their Flame-retardant Effects on Paper

Lizheng Sha, Kefu Chen


Ammonium polyphosphate (APP) was synthesized by heating a mixture of phosphoric acid and urea, and APP/diatomite composite flame-retardant fillers were prepared by two methods: mixing and in situ polymerization. Flame-retardant paper was made by adding the prepared composite fillers to paper. The APP and APP/diatomite composite fillers were characterized by XRD, 31PNMR, SEM, FTIR, and TG. The flame retardation of paper containing these composite fillers was determined. Results showed that the prepared APP had a minimum solubility when the molar ratio of phosphoric acid to urea was 1:1.8. Under these conditions, its degree of polymerization was 91.21. After mixing and in situ polymerization, a large amount of APP was adsorbed into the surface of the diatomite. These two APP/diatomite composite fillers had similar thermal stabilities, but the flame retardation of paper containing in situ polymerized composite filler was better than that of paper containing the composite filler obtained by mixing.


Ammonium polyphosphate; Diatomite; In situ polymerization; Composite flame-retardant filler; Flame retardation

Full Text: PDF

Welcome to BioResources! This online, peer-reviewed journal is devoted to the science and engineering of biomaterials and chemicals from lignocellulosic sources for new end uses and new capabilities. The editors of BioResources would be very happy to assist you during the process of submitting or reviewing articles. Please note that logging in is required in order to submit or review articles. Martin A. Hubbe, (919) 513-3022,; Lucian A. Lucia, (919) 515-7707, URLs:; ISSN: 1930-2126