Damage Mode and Failure Mechanism of Starch-based Aqueous Polymer Isocyanate Plywood Bonded Structure

Wenbiao Xu, Junyou Shi, Shumin Wang

Abstract


Aging means that a polymer material’s performance gradually deteriorates, with the loss of use value due to the comprehensive effect of internal and external factors. In this work, a starch-based aqueous polymer isocyanate (API) adhesive joint structure of crosslinking in bonding interface was investigated. The compression shear strength was recognized as a key evaluation index, and the hygrothermal aging experiment tests were accelerated to study the damage mode and failure mechanism of the glue joint structure. The results showed that the adhesive properties of fracture were ductile fracture, and with an increase of aging time, the damage mode of the bonding was transformed from a cohesion damage mode to a cohesion damage with interface damage mode. In the early stages of the aging tests, the effect of temperature on the compression shear strength was most important; however, with the increase of aging time, the effect of humidity became most important.

Keywords


Bonding; Accelerated aging; Fracture; Damage mode

Full Text: PDF

Welcome to BioResources! This online, peer-reviewed journal is devoted to the science and engineering of biomaterials and chemicals from lignocellulosic sources for new end uses and new capabilities. The editors of BioResources would be very happy to assist you during the process of submitting or reviewing articles. Please note that logging in is required in order to submit or review articles. Martin A. Hubbe, (919) 513-3022, hubbe@ncsu.edu; Lucian A. Lucia, (919) 515-7707, lucian.lucia@gmail.com URLs: bioresourcesjournal.com; http://ncsu.edu/bioresources ISSN: 1930-2126