Thermal Stability and Degradation of Poly (Lactic Acid) / Hexamoll® DINCH / Montmorillonite Composites

Zhi-Guo Zhang, Ri-Heng Song, Gui-Lin Hu, Yao-Yu Sun


The effects of the plasticizer 1,2-cyclohexane dicarboxylic acid diisononyl ester (Hexamoll® DINCH) on the thermal stability and degradation of poly (lactic acid) were investigated and compared with tributyl citrate and montmorillonite. A series of poly (lactic acid) composites were prepared via melt blending before being hot pressed into 0.3 mm films. Along with the increase of the content of MMT, the agglomeration degree rise and the MMT content for this study was determined. The addition of Hexamoll® DINCH could efficiently decrease the Tg of PLA and improve the crystallinity of poly (lactic acid) composites. The addition of DINCH or TBC could deteriorate the thermal stability of PLA composites. The addition of montmorillonite could improve the thermal stability of PLA/TBC and PLA/DINCH composites. The kinetic parameters including activation energy of decomposition (E), reaction order (n), and pre-exponential factor (lnA) of PLA/DINCH/MMT composites are 180.2 kJ/mol, 0.863, and 36.8, respectively by using Freeman-Carroll method.


Poly (lactic acid); Thermal stability; Hexamoll® DINCH; Kinetic parameter; Montmorillonite

Full Text: PDF

Welcome to BioResources! This online, peer-reviewed journal is devoted to the science and engineering of biomaterials and chemicals from lignocellulosic sources for new end uses and new capabilities. The editors of BioResources would be very happy to assist you during the process of submitting or reviewing articles. Please note that logging in is required in order to submit or review articles. Martin A. Hubbe, (919) 513-3022,; Lucian A. Lucia, (919) 515-7707, URLs:; ISSN: 1930-2126