Micromechanical Properties of the Interphase in Cellulose Nanofiber-reinforced Phenol Formaldehyde Bondlines

Cong Liu, Yang Zhang, Siqun Wang, Yujie Meng, Omid Hosseinaei

Abstract


Lab-processed cellulose nanofibrils (CNF-L), commercial cellulose nanofibrils (CNF-C), and cellulose nanocrystals (CNC) were used in this study as reinforcing materials in phenol formaldehyde (PF) resin. The mechanical modification of adhesives and cell wall layers (S2 and compound corner-middle lamellae [CCML]) by the three types of cellulose particles was investigated by nanoindentation. Results showed that cellulose nano-materials can improve the mechanical properties of both adhesives and the cell wall structure. CNF-C had the most obvious reinforcing effect on the elastic modulus (Er) and hardness within the glue line. With modification, the Er and hardness reached 13.0 and 0.436 GPa, respectively, in the S2 layer far from the glue line. In comparison, the control sample had an Er and hardness of 7.31 and 0.256 GPa, respectively.

Keywords


Cellulose nanomaterials; PF resin; Mechanical properties; Nanoindentation; Cell wall

Full Text: PDF

Welcome to BioResources! This online, peer-reviewed journal is devoted to the science and engineering of biomaterials and chemicals from lignocellulosic sources for new end uses and new capabilities. The editors of BioResources would be very happy to assist you during the process of submitting or reviewing articles. Please note that logging in is required in order to submit or review articles. Martin A. Hubbe, (919) 513-3022, hubbe@ncsu.edu; Lucian A. Lucia, (919) 515-7707, lucian.lucia@gmail.com URLs: bioresourcesjournal.com; http://ncsu.edu/bioresources ISSN: 1930-2126