Performance of Concrete Made with Superplasticizer from Modified Black Liquor and Polycarboxylate

Tailong Zhang, Jianming Gao, Bing Qi, Yanling Liu

Abstract


A new kind of retarding polycarboxylate superplasticizer (M20S80) was prepared through the modification of black liquor and polycarboxylate superplasticizer (S) through an Fe2+-H2O2 reaction system. The synthesis process of M20S80 was introduced. Infrared spectrum analysis (FT-IR) was used to investigate the changes in functional groups in M20S80. At the same time, a mixture of LM20S80 was made by mixing black liquor and S at a mass ratio of 1:4 directly at room temperature. In comparison with S and LM20S80, the influences of M20S80 on the properties of concrete were studied. The results indicate that M20S80 had a better water reduction rate in concrete than LM20280 and was close to S under the same conditions. Furthermore, M20S80 had a retarding effect on the early strength development of concrete, but no negative influence on strength after 28 d of curing. Finally, M20S80 with dosages of 0.45% appeared to be more effective in improving the pore structure of concrete.

Keywords


Black liquor; Polycarboxylate superplasticizer; Chemical modification; Concrete; Infrared spectrum analysis

Full Text: PDF

Welcome to BioResources! This online, peer-reviewed journal is devoted to the science and engineering of biomaterials and chemicals from lignocellulosic sources for new end uses and new capabilities. The editors of BioResources would be very happy to assist you during the process of submitting or reviewing articles. Please note that logging in is required in order to submit or review articles. Martin A. Hubbe, (919) 513-3022, hubbe@ncsu.edu; Lucian A. Lucia, (919) 515-7707, lucian.lucia@gmail.com URLs: bioresourcesjournal.com; http://ncsu.edu/bioresources ISSN: 1930-2126