Fabrication of Magnetic and EMI Shielding Wood-Based Composite by Electroless Ni-Fe-P Plating Process

Li Wang, Changhong Shi, Lijuan Wang

Abstract


A Ni-Fe-P alloy coating was applied to Triplochiton scleroxylon veneers to prepare a magnetic, corrosion-resistant, electromagnetism-shielding wood-based composite. The effects of solution pH on metal deposition, surface resistivity, crystal structure, and the chemical composition of the coatings were investigated. The electro-conductivity, anti-corrosion properties, and magnetic and electromagnetic shielding performances were also measured. The results showed that increasing the pH favored the co-deposition of nickel and iron; metal deposition increased and surface resistivity decreased. The Ni-Fe-P alloy coatings obtained at pH values between 8.8 and 9.6 were all crystalline. VSM data revealed that the addition of elemental Fe to the deposits remarkably increased the magnetic properties of the products. The anti-corrosion properties of Ni-Fe-P coatings were higher than those of Ni-P coatings prepared in 3.5 wt.% NaCl solution. The electromagnetic shielding effectiveness value of Ni-Fe-P plated veneer reached 45 to 60 dB at frequencies ranging from 9 kHz to 1.5 GHz.

Keywords


Triplochiton scleroxylon; Electroless Ni-Fe-P plating; Magnetic; Corrosion resistance; Electromagnetic shielding effectiveness

Full Text: PDF

Welcome to BioResources! This online, peer-reviewed journal is devoted to the science and engineering of biomaterials and chemicals from lignocellulosic sources for new end uses and new capabilities. The editors of BioResources would be very happy to assist you during the process of submitting or reviewing articles. Please note that logging in is required in order to submit or review articles. Martin A. Hubbe, (919) 513-3022, hubbe@ncsu.edu; Lucian A. Lucia, (919) 515-7707, lucian.lucia@gmail.com URLs: bioresourcesjournal.com; http://ncsu.edu/bioresources ISSN: 1930-2126