Microstructural, Mechanical, and Physicochemical Behaviours of Alkali Pre-treated Oil Palm Stalk Fibres

Loo Yu Xiang, Suhaiza Hanim Hanipah, Mohd Afandi P. Mohammed, Azhari Samsu Baharuddin, Azwan Mat Lazim


The effect of alkali pre-treatment (sodium hydroxide, NaOH) on the microstructural, mechanical, and chemical composition of oil palm stalk fibres (OPSF) is reported for future bioconversion processes. The OPSF was pre-treated with various concentrations of NaOH (5, 10, 20, 30, and 40% w/v). Scanning electron microscopy analysis revealed that 5% w/v alkali concentration caused complete removal of silica bodies and waxy layers, whereas pronounced degradation of the fibres occurred at 40% w/v NaOH concentration. Mechanical test results showed that the maximum elastic modulus of untreated OPSF was 2.5 GPa and the modulus was not sensitive to alkali concentration. Permanent set (plastic strain) and viscoelastic behaviours of OPSF were observed from the loading-unloading and stress relaxation test results, respectively. Agreement was observed between the Prony series viscoelastic model and test results, which provided further evidence of the viscoelastic behaviour of OPSF.


Oil palm stalk fibres (OPSF); Pre-treatment; Sodium hydroxide (NaOH); Mechanical behaviours; Morphology; Lignocellulosic composition

Full Text: PDF

Welcome to BioResources! This online, peer-reviewed journal is devoted to the science and engineering of biomaterials and chemicals from lignocellulosic sources for new end uses and new capabilities. The editors of BioResources would be very happy to assist you during the process of submitting or reviewing articles. Please note that logging in is required in order to submit or review articles. Martin A. Hubbe, (919) 513-3022, hubbe@ncsu.edu; Lucian A. Lucia, (919) 515-7707, lucian.lucia@gmail.com URLs: bioresourcesjournal.com; http://ncsu.edu/bioresources ISSN: 1930-2126