Preparation and Properties of Kraft Lignin-N-Isopropyl Acrylamide Hydrogel

Huachao Luo, Shixue Ren, Yanli Ma, Guizhen Fang, Guiquan Jiang

Abstract


Kraft lignin was used to prepare kraft lignin-N-isopropyl acrylamide hydrogel (KNIAH). The results indicated that using a 1:2 mass ratio of KL-to-N-isopropyl acrylamide (NIPAM), 48 h reaction time, and 1.5 mL of crosslinking agent yielded KNIAH with the maximum swelling degree (209.3%). The crosslinking reaction was verified by C-N shifting at 1272 cm-1 and increased C=O bonding at 1720 cm-1. KNIAH with a smooth and uniform surface was created. DSC demonstrated that free water combined with KNIAH at 200 °C, after which KNIAH began exothermic decomposition. TGA shows that KNIAH with good performance of heat resistance and degradation. Absorption was maximized at 20 °C; low temperature and neutral solution was conducive to water absorption. Decolorization increased with decreasing concentration and pH value.

Keywords


Gels; Grafting; Copolymers; Crosslinking

Full Text: PDF

Welcome to BioResources! This online, peer-reviewed journal is devoted to the science and engineering of biomaterials and chemicals from lignocellulosic sources for new end uses and new capabilities. The editors of BioResources would be very happy to assist you during the process of submitting or reviewing articles. Please note that logging in is required in order to submit or review articles. Martin A. Hubbe, (919) 513-3022, hubbe@ncsu.edu; Lucian A. Lucia, (919) 515-7707, lucian.lucia@gmail.com URLs: bioresourcesjournal.com; http://ncsu.edu/bioresources ISSN: 1930-2126