Effects of Treatment Temperature on Properties of Starch-based Adhesives

Hongwei Yu, Yuan Cao, Qun Fang, Zhikun Liu

Abstract


Starch-based adhesives were developed by hydrolyzing starch with polyvinyl alcohol under alkaline and acidic conditions at various treatment temperatures. The chemical and physical structures of the corn starch and hydrolyzed starch were characterized with Fourier Transform infrared (FT-IR) spectroscopy, X-ray diffraction (XRD), and scanning electronic microscopy (SEM). Thermal degradation and bond strength were also evaluated. The results indicated that the bond strength of starch adhesives reached a maximum value at 40 °C. The FI-IR results showed that the amount of hydroxyl groups first increased and then decreased with increasing treatment temperature. When the treatment temperature was 55 °C the crystallinity of treated starch was the lowest and the thermal resistance also the weakest; it decreased by 10.1% and 13.6% respectively compared to untreated starch. Obvious erosion could be observed from the SEM images of treated starch. In addition, the interaction of polyvinyl alcohol (PVA) and starch also could be observed, and the results indicated that the compatibility between starch and PVA became better and better as the treated temperature was increased.

Keywords


Starch adhesive; Acidic and alkaline treatment; Treatment temperature; Structure; Bond strength

Full Text: PDF

Welcome to BioResources! This online, peer-reviewed journal is devoted to the science and engineering of biomaterials and chemicals from lignocellulosic sources for new end uses and new capabilities. The editors of BioResources would be very happy to assist you during the process of submitting or reviewing articles. Please note that logging in is required in order to submit or review articles. Martin A. Hubbe, (919) 513-3022, hubbe@ncsu.edu; Lucian A. Lucia, (919) 515-7707, lucian.lucia@gmail.com URLs: bioresourcesjournal.com; http://ncsu.edu/bioresources ISSN: 1930-2126