Modification of Lignin with Silane Coupling Agent to Improve the Interface of Poly(L-lactic) Acid/Lignin Composites

Jun Zhu, Liyuan Xue, Wei Wei, Chunyu Mu, Man Jiang, Zuowan Zhou

Abstract


To improve the mechanical properties of lignin-filled poly(L-lactic) composites, three silane coupling agents, 3-aminopropyltriethoxysilane (KH550), γ-glycidoxypropyltrimethoxysilane (KH560), and g-methyacryl-oxypropyltrimethoxysilane (KH570), were treated systematically with different solvents to modify the interfacial connections. The treatment of lignin with 2 wt.% aqueous KH550 solution was proved to be the most successful. Chemical bonding between the filler and the matrix was formed, according to the FTIR spectra. Furthermore, scanning electron microscope images showed that such treated lignin particles dispersed well in the composites. The tensile strength and Young’s modulus of the composite improved significantly from 55.1 and 1589 MPa to 67.0 and 1641 MPa, respectively, with 5 wt.% treated lignin addition. Although its elongation at break decreased from 20.3 to 12.4% after 5 wt.% of the treated lignin was added, it was still better than that of poly(L-lactic acid) without any additive (10.3%).

Keywords


Poly(L-lactic) acid/lignin bio-composites; Silane coupling agent; Interfacial modification; Mechanical properties

Full Text: PDF

Welcome to BioResources! This online, peer-reviewed journal is devoted to the science and engineering of biomaterials and chemicals from lignocellulosic sources for new end uses and new capabilities. The editors of BioResources would be very happy to assist you during the process of submitting or reviewing articles. Please note that logging in is required in order to submit or review articles. Martin A. Hubbe, (919) 513-3022, hubbe@ncsu.edu; Lucian A. Lucia, (919) 515-7707, lucian.lucia@gmail.com URLs: bioresourcesjournal.com; http://ncsu.edu/bioresources ISSN: 1930-2126