Evaluation of Mechanical Properties of Reinforced Poplar Laminated Veneer Lumber

Jie Wang, Xiaolei Guo, Wei Zhong, Huiyun Wang, Pingxiang Cao

Abstract


Three types of reinforcement materials, a carbon fiber-reinforced polymer (CFRP) sheet, a glass fiber-reinforced polymer (GFRP) mesh, and a composite of the CFRP sheet and GFRP mesh, were used to reinforce poplar laminated veneer lumber (LVL), and the multi-step hot-pressing method was also applied. The mechanical properties, i.e., modulus of rupture (MOR), modulus of elasticity (MOE), and horizontal shear strength (HSS), of the reinforced LVL were investigated, as well as the effects of lay-up location of the CFRP sheet/GFRP mesh composite. The results indicated that applying the multi-step hot-pressing method and incorporating the CFRP sheet, GFRP mesh, and the CFRP sheet/GFRP mesh composite noticeably improved the MOR and MOE under horizontal and vertical loadings. Only the multi-step hot-pressing method was able to greatly improve the HSS of reinforced LVL under both loading modes. The improved effect of the three kinds of reinforcing materials on the mechanical properties was ordered as follows: CFRP sheet/GFRP mesh composite > CFRP sheet > GFRP mesh. Locating the CFRP sheet/GFRP mesh composite closer to the surface veneer layer yielded the best mechanical properties for the reinforced poplar LVL.

Keywords


Poplar laminated veneer lumber; Carbon fiber sheet; Glass fiber mesh; Multi-step hot pressing method; Mechanical properties

Full Text: PDF

Welcome to BioResources! This online, peer-reviewed journal is devoted to the science and engineering of biomaterials and chemicals from lignocellulosic sources for new end uses and new capabilities. The editors of BioResources would be very happy to assist you during the process of submitting or reviewing articles. Please note that logging in is required in order to submit or review articles. Martin A. Hubbe, (919) 513-3022, hubbe@ncsu.edu; Lucian A. Lucia, (919) 515-7707, lucian.lucia@gmail.com URLs: bioresourcesjournal.com; http://ncsu.edu/bioresources ISSN: 1930-2126