Mechanical Properties and Morphology of Wood Plastic Composites Produced with Thermally Treated Beech Wood

Farhad Arwinfar, Seyyed Khalil Hosseinihashemi, Ahmad Jahan Latibari, Amir Lashgari, Nadir Ayrilmis

Abstract


The effect of thermal-treatment severity of wood on the mechanical and morphological properties of wood plastic composites (WPCs) was investigated. Wood chips were first heat treated at 120, 150, or 180 ºC for 30 or 120 min under saturated steam in a digester. The composites were composed of thermally treated and untreated wood flour, polypropylene, and a coupling agent, produced by melt compounding and then injection molding. The thermal-treatment of the beech wood improved some mechanical properties of the WPCs, depending on the treatment-time and temperature. The SEM micrographs of the composites showed that the outer surface of the wood fiber was coated by a section of amorphous lignin. The SEM images showed that the WPCs produced from the wood treated at 150 ºC for 30 min had considerably fewer holes and many broken fiber ends embedded in the polymer matrix, indicating better compatibility between the wood flour and the polymer matrix. Based on the results of the mechanical testing of the WPCs, the optimum thermal-treatment for WPC production was 150 °C for 30 min.

Keywords


Thermal; Heat treatment; Mechanical properties; Wood-polypropylene

Full Text: PDF

Welcome to BioResources! This online, peer-reviewed journal is devoted to the science and engineering of biomaterials and chemicals from lignocellulosic sources for new end uses and new capabilities. The editors of BioResources would be very happy to assist you during the process of submitting or reviewing articles. Please note that logging in is required in order to submit or review articles. Martin A. Hubbe, (919) 513-3022, hubbe@ncsu.edu; Lucian A. Lucia, (919) 515-7707, lucian.lucia@gmail.com URLs: bioresourcesjournal.com; http://ncsu.edu/bioresources ISSN: 1930-2126