Determination of Screw Withdrawal Strength of Heat-Treated and Reinforced Laminated Veneer Lumber

Osman Perçin

Abstract


The withdrawal resistance of screws in heat-treated and reinforced laminated veneer lumber (RLVL) was determined in the radial, tangential, and transverse directions. For this reason, laminated veneer lumber (LVL) and RLVL with carbon fibers were produced from heat-treated oak (Quercus petraea (Liebl.)) veneers using phenol formaldehyde as the adhesive. Wood samples were heat-treated at 140, 170, 200, and 230 °C for 2 h. According to the results of the study, screw withdrawal strength values of LVL increased for heat-treated samples at 140 °C, but decreased at 170, 200, and 230 °C. However, in all groups, the screw withdrawal strength values of the RLVL were higher than those of the LVL. The highest screw withdrawal strength values were identified in the tangential direction, and the lowest were in the transverse directions. Carbon fiber can be used between the heat-treated wood veneers to provide sufficient screw withdrawal strength for use in many different industries.

Keywords


Laminated veneer lumber; Heat treatment; Screw withdrawal strength; Carbon fiber

Full Text: PDF

Welcome to BioResources! This online, peer-reviewed journal is devoted to the science and engineering of biomaterials and chemicals from lignocellulosic sources for new end uses and new capabilities. The editors of BioResources would be very happy to assist you during the process of submitting or reviewing articles. Please note that logging in is required in order to submit or review articles. Martin A. Hubbe, (919) 513-3022, hubbe@ncsu.edu; Lucian A. Lucia, (919) 515-7707, lucian.lucia@gmail.com URLs: bioresourcesjournal.com; http://ncsu.edu/bioresources ISSN: 1930-2126