The Effects of UV-A on Dry Rice Straw Decomposition under Controlled Laboratory Conditions

Yunlong Li, Hongying Huang, Guofeng Wu, Shuzhen Yan, Zhizhou Chang, Jinhua Bi, Le Chen


In arid and semi-arid areas, organic matter decomposition is stimulated by ultraviolet radiation. In this paper, the association between straw decomposition and UV-A exposure was evaluated. Oven-dried rice straw samples were chronically exposed to UV-A radiation and examined periodically for up to 90 days at room temperature. Scanning electron microscopy (SEM) showed that noticeable disintegration of the fiber structure occurred on the irradiated sample surface in comparison to the control. At the end of the UV-A treatment period, straw mass had decreased by 5%, and dissolved organic carbon (DOC) increased by 18%. The content of cellulose, hemicellulose, and lignin of the irradiated straw decreased by 29.3%, 14.4% and 49.3%, respectively. The marked loss of nitrogen and potassium in the exposed straw were also observed. Thermogravimetric analysis (TGA) showed that treatment with UV-A radiation tended to decrease the mass loss rate and the thermal degradation temperature of the straw biomass from 220 °C to 208 °C. Infrared spectrometric analysis (ATR-FTIR) showed that functional groups, e.g., C–OH and C–O–C, were disrupted obviously due to UV-A exposure. These results suggest that ultraviolet-A irradiation facilitates straw decomposition by direct photochemical degradation.


Ultraviolet-A irradiation; Rice straw photodegradation; Straw chemical composition; TGA; ATR-FTIR

Full Text: PDF

Welcome to BioResources! This online, peer-reviewed journal is devoted to the science and engineering of biomaterials and chemicals from lignocellulosic sources for new end uses and new capabilities. The editors of BioResources would be very happy to assist you during the process of submitting or reviewing articles. Please note that logging in is required in order to submit or review articles. Martin A. Hubbe, (919) 513-3022,; Lucian A. Lucia, (919) 515-7707, URLs:; ISSN: 1930-2126