Biomorphic Charcoal/TiO2 Composites from Poplar Templates

Liangcun Qian, Peirong Chen, Rui Li, Lin Mei, Yamei Liu, Geli Wu, Shengquan Liu

Abstract


Biomorphic charcoal/TiO2 composites (C/TiO2) were produced from poplar templates. The poplar templates were impregnated with butyl titanate sol with a vacuum/positive pressure technology. From the anatomic structure of poplar and fluid thermodynamics, the alternative vacuum/positive pressure technology was an efficient method of infiltrating bio-templates with sol and overcoming the embolization effect of the sol in capillaries. After sol infiltration, the maximum density of the poplar was approximately 0.958 ± 0.005 g/cm3. Using X-ray diffraction (XRD), thermogravimetric data (TG-DTG), and scanning electron microscopy (SEM), it was found that the pore sizes in the cell walls of C/TiO2 were, respectively, 30 to 150, 3 to 15, and 1.5 μm, and a surprising mesoporous-like honeycomb structure formed at approximately 800 °C in a N2 atmosphere. The phase structure of C/TiO2 shifted from anatase to rutile between 700 and 900 °C in N2. Furthermore, the temperature of the maximum combustion rates of C/TiO2 sintered at 800 °C in N2 was approximately 610 °C. The average shrinkage values from the native poplar to C/TiO2 along the radial, tangential, and axial directions were 28.53%, 21.80%, and 17.03%, respectively.

Keywords


Mesoporous; Biomorphic C/TiO2 composites; Anisotropic; Vacuum technology

Full Text: PDF

Welcome to BioResources! This online, peer-reviewed journal is devoted to the science and engineering of biomaterials and chemicals from lignocellulosic sources for new end uses and new capabilities. The editors of BioResources would be very happy to assist you during the process of submitting or reviewing articles. Please note that logging in is required in order to submit or review articles. Martin A. Hubbe, (919) 513-3022, hubbe@ncsu.edu; Lucian A. Lucia, (919) 515-7707, lucian.lucia@gmail.com URLs: bioresourcesjournal.com; http://ncsu.edu/bioresources ISSN: 1930-2126