Electromagnetic Shielding Performance of Nickel Plated Expanded Graphite/Wood Fiber Composite

Yi Chen, Chuwang Su, Quanping Yuan, Manjun Zhan, Bing Yang, Junwei Xia

Abstract


To develop a wood-based electromagnetic shielding composite, in-situ electroless plating was used to plate nickel onto the surface of expanded graphite (EG) to obtain nickel-plated EG (Ni-EG), and the Ni-EG was mixed with wood fiber to manufacture the composite. The optimal plating formula was as follows: 20 g/L NiSO4·6H2O as the main salt, 60 g/L N2H4·H2O as the reducing agent, 50 g/L Na3C6H5O7·2H2O as the complexing agent, 40 g/L CH3COONa·H2O as the buffering agent, pH value 11, and a temperature of 90 °C. These conditions yielded the highest quality of nickel coating (3.57 g). As EG concentration increased from 2 to 10 g/L, the percentage of the Ni-EG in the composite was 60%, the thickness of the composite was 2 mm, the density was 0.9 g/cm3, the magnetic properties and resistivity of the Ni-EG decreased from 29.5 to 5.57 emu/g and 80.2 to 10.7 mΩ·cm, respectively, and the electromagnetic shielding effectiveness (SE) and the reflectivity of the composite increased from 55 to 60 dB and −3.6 to -1.8 dB, respectively. Consequently, the introduction of nickel is suitable for improving the absorbing performance of Ni-EG/wood fiber composites, leading to better SE in a broad frequency range.

Keywords


Expanded graphite; Chemical nickel plating; Wood fiber; Shielding effectiveness; Reflectivity

Full Text: PDF

Welcome to BioResources! This online, peer-reviewed journal is devoted to the science and engineering of biomaterials and chemicals from lignocellulosic sources for new end uses and new capabilities. The editors of BioResources would be very happy to assist you during the process of submitting or reviewing articles. Please note that logging in is required in order to submit or review articles. Martin A. Hubbe, (919) 513-3022, hubbe@ncsu.edu; Lucian A. Lucia, (919) 515-7707, lucian.lucia@gmail.com URLs: bioresourcesjournal.com; http://ncsu.edu/bioresources ISSN: 1930-2126