Synthesis of Biomorphic Charcoal/TiO2 Composites from Moso Bamboo Templates for Absorbing Microwave

Liangcun Qian, Shuyun Yang, Weining Hong, Peirong Chen, Xiaolin Yao


Biomorphic charcoal/TiO2 composites (C/TiO2) from moso bamboo templates were produced for absorbing microwave. Subsequently, the characteristics of the C/TiO2 were investigated by scanning electron microscopy, thermogravimetric analysis, and vector network analysis. The results showed that the biomorphic microstructure of the moso bamboo charcoal was duplicated in the C/TiO2. Thus, the density of the C/TiO2 sintered at 1200 °C was lower and approximately 0.916 ± 0.003 g/cm3. Moreover, the ignition, the maximum combustion, and the burnout temperatures of the C/TiO2 sintered at 600 °C were ~320 °C, ~530 °C, and ~585 °C, respectively. Additionally, with the rising of the temperature sintering C/TiO2, the microwave absorbency of the C/TiO2 was improved over high frequency zones. Furthermore, the average imaginary-part values of the permittivity of the C/TiO2 sintered at 600 °C and 1200 °C notably increased by 11.16-fold. In addition, the peak of microwave reflection loss of the samples (2.0 mm thickness) from the C/TiO2 powder (wt. 20%) sintered at 1200 °C and the paraffin wax (wt. 80%) was observed as -18.0 dB at 17.4 GHz. Therefore, the C/TiO2 sintered at higher temperatures exhibited lower geometrical density, better thermostability, and favorable microwave absorptive properties.


Biomorphic; Charcoal/TiO2 composites; Moso bamboo; Thermostability; Microwave-absorbing properties

Full Text: PDF

Welcome to BioResources! This online, peer-reviewed journal is devoted to the science and engineering of biomaterials and chemicals from lignocellulosic sources for new end uses and new capabilities. The editors of BioResources would be very happy to assist you during the process of submitting or reviewing articles. Please note that logging in is required in order to submit or review articles. Martin A. Hubbe, (919) 513-3022,; Lucian A. Lucia, (919) 515-7707, URLs:; ISSN: 1930-2126