Complete Dissolution of Ball-Milled Masson Pine Using an Aqueous Sodium Hydroxide Solvent

Yangsu Zhu, Lingfeng Yang, Wenjuan Wu, Zhiguo Wang, Yongcan Jin

Abstract


An inorganic sodium hydroxide aqueous solution was developed for the dissolution of ball-milled softwood. Extractive-free Masson pine powder was prepared from the wood meal by planetary ball milling for various lengths of time. The effects of ball milling on the dissolution and regeneration of Masson pine powder were investigated. After 4 h of ball milling, the wood powder was completely dissolved in 6 wt% NaOH aqueous solution under vigorous magnetic stirring for 10 to 20 min at room temperature. The alkaline nitrobenzene oxidation products yield of 4 h ball-milled wood was very close to that of coarse wood meal without ball milling. Regeneration of the lignin fraction was easier than cellulose during the acid neutralization process, and the dialysis regeneration yield of total biomass was 91.1%. Therefore, the complete dissolution of the Masson pine in sodium hydroxide solution is of great potential for enhancing lignin isolation with a very little structural change.

Keywords


Masson pine; Sodium hydroxide aqueous solution; Ball milling; Dissolution; Regeneration

Full Text: PDF

Welcome to BioResources! This online, peer-reviewed journal is devoted to the science and engineering of biomaterials and chemicals from lignocellulosic sources for new end uses and new capabilities. The editors of BioResources would be very happy to assist you during the process of submitting or reviewing articles. Please note that logging in is required in order to submit or review articles. Martin A. Hubbe, (919) 513-3022, hubbe@ncsu.edu; Lucian A. Lucia, (919) 515-7707, lucian.lucia@gmail.com URLs: bioresourcesjournal.com; http://ncsu.edu/bioresources ISSN: 1930-2126