Preparation and Characterization of Aldehyde-Functionalized Cellulosic Fibers through Periodate Oxidization of Bamboo Pulp

Jinguang Wei, Chungui Du, Hongzhi Liu, Yufei Chen, Huilong Yu, Zhongxi Zhou

Abstract


Cellulosic fibers were efficiently disintegrated from bamboo pulp as raw material and then oxidized using sodium periodate to introduce dialdehyde groups on their surfaces. The resultant fibers were characterized using Fourier transform infrared spectroscopy (FT-IR), X-ray diffraction (XRD), and thermogravimetric analysis (TGA). FT-IR spectra demonstrated that the characteristic absorption band of aldehyde groups was present at 1735 cm-1, confirming that aldehyde groups were successfully introduced. XRD showed that the nature of bamboo pulp fibers changed slightly after oxidation, except in the reduction of crystallinity. The aldehyde content increased with the sodium periodate content and reached a maximum of 1.41 mmol/g. The yield loss maximum was 32.4 wt%. TGA results showed that the temperature at the initial and final decomposition of the oxidized fibers was subject to the periodate dosage and that the thermal stability decreased to some extent.

Keywords


Bamboo pulp fibers; Periodate oxidization; FT-IR; XRD; TGA

Full Text: PDF

Welcome to BioResources! This online, peer-reviewed journal is devoted to the science and engineering of biomaterials and chemicals from lignocellulosic sources for new end uses and new capabilities. The editors of BioResources would be very happy to assist you during the process of submitting or reviewing articles. Please note that logging in is required in order to submit or review articles. Martin A. Hubbe, (919) 513-3022, hubbe@ncsu.edu; Lucian A. Lucia, (919) 515-7707, lucian.lucia@gmail.com URLs: bioresourcesjournal.com; http://ncsu.edu/bioresources ISSN: 1930-2126