Manufacture of Low-cost Activated Carbon Using Sago Palm Bark and Date Pits by Physiochemical Activation

Iqbal Khalaf Erabee, Amimul Ahsan, Nik Norsyahariati Nik Daud, Syazwani Idrus, Shahriar Shams, Mohd Fadhil Md Din, Shahabaldin Rezania

Abstract


Two raw materials, sago palm bark (SPB) and date pits, were utilized as precursors to prepare high porosity activated carbon (AC). The porosity of these two raw materials was compared with that of commercial AC made from coconut shells. The physicochemical activation method was used for AC preparation, and it consisted of two steps, carbonization and activation. The activation process was performed using zinc chloride (ZnCl2) as an activation agent. N2 adsorption-desorption analysis was carried out to characterize the porosity of AC. Thermogravimetric analysis (TGA) was conducted for the two raw materials. The adsorbent made from SPB, which showed the maximum surface area of 1634 m2/g at the 700 °C activation temperature for one hour, while the surface area of prepared AC from date pits was 1367 m2/g. Both prepared ACs had a larger surface area than commercial AC made with coconut shell (1348 m2/g).

Keywords


Activated carbon; Date pits; Sago palm bark; Porosity characterization; Activation

Full Text: PDF

Welcome to BioResources! This online, peer-reviewed journal is devoted to the science and engineering of biomaterials and chemicals from lignocellulosic sources for new end uses and new capabilities. The editors of BioResources would be very happy to assist you during the process of submitting or reviewing articles. Please note that logging in is required in order to submit or review articles. Martin A. Hubbe, (919) 513-3022, hubbe@ncsu.edu; Lucian A. Lucia, (919) 515-7707, lucian.lucia@gmail.com URLs: bioresourcesjournal.com; http://ncsu.edu/bioresources ISSN: 1930-2126