Characterizing Microscopic Changes of Paulownia Wood under Thermal Compression

Dilek Dogu, Fatma Digdem Tuncer, Davut Bakir, Zeki Candan

Abstract


This study evaluates the microscopic changes of paulownia solid wood panels subjected to thermal compression via characterizing the changes in wood microstructure. The panels, with dimensions of 500 mm × 100 mm × 20 mm, were hot-pressed in a tangential direction by using a laboratory-type hot press at a temperature of either 150 °C or 170 °C and a pressure of 2 MPa for 45 min. Microscopic investigations conducted by light microscopy showed that slightly more damage occurred in the samples compressed at 170 °C and 2 MPa than at 150 °C and 2 MPa, and that the distribution of deformation in the panels was not uniform in the growth rings of the two treatment groups. The cell collapse was not observed in the microstructure of paulownia wood after the thermal compression. Cell shapes and their arrangement in the growth ring alongside loading direction were interpreted as effective factors governing the non-uniform distribution of damage and the lack of cell collapse in the microstructure.

Keywords


Paulownia wood; Thermally compressed wood; Wood microstructure; Wood densification; Cell collapse; Cellular failures

Full Text: PDF

Welcome to BioResources! This online, peer-reviewed journal is devoted to the science and engineering of biomaterials and chemicals from lignocellulosic sources for new end uses and new capabilities. The editors of BioResources would be very happy to assist you during the process of submitting or reviewing articles. Please note that logging in is required in order to submit or review articles. Martin A. Hubbe, (919) 513-3022, hubbe@ncsu.edu; Lucian A. Lucia, (919) 515-7707, lucian.lucia@gmail.com URLs: bioresourcesjournal.com; http://ncsu.edu/bioresources ISSN: 1930-2126