Synergistic Flame Retardant Effects of Different Zeolites on Intumescent Fire Retardant Coating for Wood

Jing Wu, Mingzhi Wang, Hongwu Guo

Abstract


To investigate the fire-retardant properties of intumescent fire-retardant coatings of wood modified by different zeolites, tests were conducted by a cone calorimeter with poplar samples whose surfaces were covered by an intumescent fire-retardant coating modified by 3A, 4A, 5A, 13X zeolites, respectively. Results indicated that the ignition time (TTI) of the intumescent fire-retardant coating modified by 3A zeolite was prolonged 120 s, while the total smoke production (TSP) increased 60.1% as compared with the untreated group. The intumescent fire-retardant coating modified by the 13X zeolite had a smaller smoke production rate (SPR) and was the last to reach the peak-SPR. Its TSP remained in a very low state until 410 s and decreased 25%. Thus, 3A zeolite and 13X zeolite were of complementarily synergistic effects on improving the fire-retardant properties of an intumescent fire-retardant coating for wood. This paper suggested the alternative types of zeolites for flame-retardant coatings.

Keywords


Wood; Zeolite; Intumescent flame-retardant coatings; Fire-retardant properties; Cone calorimeter

Full Text: PDF

Welcome to BioResources! This online, peer-reviewed journal is devoted to the science and engineering of biomaterials and chemicals from lignocellulosic sources for new end uses and new capabilities. The editors of BioResources would be very happy to assist you during the process of submitting or reviewing articles. Please note that logging in is required in order to submit or review articles. Martin A. Hubbe, (919) 513-3022, hubbe@ncsu.edu; Lucian A. Lucia, (919) 515-7707, lucian.lucia@gmail.com URLs: bioresourcesjournal.com; http://ncsu.edu/bioresources ISSN: 1930-2126