Effects of Fiber Size and Fiber Content on Mechanical and Physical Properties of Mengkuang Reinforced Thermoplastic Natural Rubber Composites

Wan Zarina Wan Mohamed, Azizah Baharum, Ishak Ahmad, Ibrahim Abdullah, Nurzam Ezdiani Zakaria


Thermoplastic mengkuang composites are an alternative material to solve environmental pollution issues associated with synthetic polymers. Mengkuang, or Pandanus atrocarpus, raw fiber was cut, dried, ground, and sieved to the required size. The fiber was filled into the matrix of natural rubber (NR) and high-density polyethylene (HDPE) by melt blending via internal mixer. The blend of HDPE/NR at 60/40 ratio with fiber sizes of 125 µm, 250 µm, and 500 µm were prepared at fiber contents of 10%, 20%, and 30%. The effects of fiber size and fiber content on the thermoplastic composite were investigated using tensile test, impact test, water absorption, and field emission scanning electron microscopy (FESEM). The maximum tensile strength and tensile modulus were obtained at 20% fiber content of 250 µm fiber size. Impact strength gradually decreased with the increased percentage of fiber content at fiber size, 125 µm and 250 µm. The highest tensile strain at break and lowest water absorption was observed at 10% fiber content for all sizes being studied. The effects of fiber size on water absorption, and percentage of fiber content on impact strength and tensile strain at break were statistically significant (p < 0.05).


Fiber size; Fiber content; Natural fiber; Thermoplastic composites

Full Text: PDF

Welcome to BioResources! This online, peer-reviewed journal is devoted to the science and engineering of biomaterials and chemicals from lignocellulosic sources for new end uses and new capabilities. The editors of BioResources would be very happy to assist you during the process of submitting or reviewing articles. Please note that logging in is required in order to submit or review articles. Martin A. Hubbe, (919) 513-3022, hubbe@ncsu.edu; Lucian A. Lucia, (919) 515-7707, lucian.lucia@gmail.com URLs: bioresourcesjournal.com; http://ncsu.edu/bioresources ISSN: 1930-2126