Catalytic Graphitization of Cellulose Using Nickel as Catalyst

Chao Chen, Kang Sun, Ao Wang, Siqun Wang, Jianchun Jiang


Microcrystalline cellulose was pyrolyzed and catalytically graphitized under temperatures ranging from 1000 °C to 1600 °C in the presence of nickel (Ni). Optimal conditions for graphitization were determined, along with the structure and conductivity of the resulting samples. The optimal conditions were identified as heating at 1400 °C for 3 h with 3 mmol Ni loading per gram of carbon. The samples obtained had excellent graphitic crystallinity comparable to that of commercial graphite. However, in the absence of Ni loading, no obvious graphitic structure appeared after heating under the same conditions, indicating that Ni was an efficient catalyst for the graphitization of cellulose-based carbon. High-resolution transparent electron microscopy (HRTEM) images showed well-defined graphitic structures of more than 30 layers with slice gaps of 0.340 nm. The conductivities of the samples treated under different temperatures varied from 27 S·cm-1 to 54 S·cm-1 under 20 MPa of pressure, and higher temperatures led to higher conductivity due to better graphitic crystallinity. This study fills an important area of research on the catalytic graphitization of cellulose and provides a reference for the preparation of other cellulose-based graphitic materials.


Catalytic graphitization; Cellulose; Nickel; Conductivity

Full Text: PDF

Welcome to BioResources! This online, peer-reviewed journal is devoted to the science and engineering of biomaterials and chemicals from lignocellulosic sources for new end uses and new capabilities. The editors of BioResources would be very happy to assist you during the process of submitting or reviewing articles. Please note that logging in is required in order to submit or review articles. Martin A. Hubbe, (919) 513-3022,; Lucian A. Lucia, (919) 515-7707, URLs:; ISSN: 1930-2126