Juha Lindfors, Jani Salmi, Janne Laine, Per Stenius


Model surfaces of alkyl ketene dimer (AKD) and alkenyl succinic anhyd-ride (ASA) were prepared by casting and spin-coating methods. The surface chemical composition and surface topography were investigated by XPS, ellipsometry, AFM and contact angle studies. Spin-coating resulted in layered structure of AKD and ASA surfaces; the molecular layer thickness of both AKD and ASA was found to be ca. 2.5 nm. To achieve a covering surface layer, an average thickness of ca. 35 nm was required. The rms roughness of the created surfaces was 1 - 6 nm. Colloidal probe adhesion measurements were performed to verify that the roughness was in a range suitable for these measurements. The high reactivity of ASA with water generated stability problems with the ASA layers and it has to be recognized that surface force measurements with ASA in aqueous environment are very difficult, if not impossible. How-ever, surfaces created in this way were found to be useful in providing explanations of earlier ASA adhesion studies. The contact angle measurements on ASA layers also indicated that it might be possible to asses the hydrolysis rate issues through a set of similar measurements.


Alkyl ketene dimer, Alkenyl succinic anhydride, Model surface, Adhesion, XPS, Ellipsometry, AFM, Contact angle

Full Text: PDF

Welcome to BioResources! This online, peer-reviewed journal is devoted to the science and engineering of biomaterials and chemicals from lignocellulosic sources for new end uses and new capabilities. The editors of BioResources would be very happy to assist you during the process of submitting or reviewing articles. Please note that logging in is required in order to submit or review articles. Martin A. Hubbe, (919) 513-3022, hubbe@ncsu.edu; Lucian A. Lucia, (919) 515-7707, lucian.lucia@gmail.com URLs: bioresourcesjournal.com; http://ncsu.edu/bioresources ISSN: 1930-2126