CHANGES IN THE CHEMICAL STRUCTURE OF THERMALLY TREATED WOOD

Ibrahim Tumen, Deniz Aydemir, Gokhan Gunduz, Birol Uner, Hakan Cetin

Abstract


Changes in the chemical structure of hornbeam and uludag fir woods during thermal treatment were investigated at three temperatures (170, 190, and 210 oC) and three durations (4, 8, and 12 hours). After thermal treatment, the extents of degradation in the chemical structure of the samples were determined, and the effects on the chemical composition of hornbeam wood and uludag fir wood were investigated. The data obtained were analyzed using variance analysis, and Tukey’s test was used to determine the changes in the chemical structure of uludag fir and hornbeam woods. The results showed that heating wood permanently changes several of its chemical structures and that the changes are mainly caused by thermal degradation of wood polymers. It was found that decreasing of the cellulose and holocelluloses ratio had a favorable effect on the interaction of the wood with moisture. According to the obtained results, hornbeam wood is affected more than uludag fir wood. For each wood, the maximum decreases of holocellulose and α-cellulose were found at 210oC for 12 hours, and the maximum increase of lignin occurred at the same treatment combination.

Keywords


Uludag fir wood; Chemical structure; Cellulose; Lignin; Solubility

Full Text:

PDF


Welcome to BioResources! This online, peer-reviewed journal is devoted to the science and engineering of biomaterials and chemicals from lignocellulosic sources for new end uses and new capabilities. The editors of BioResources would be very happy to assist you during the process of submitting or reviewing articles. Please note that logging in is required in order to submit or review articles. Martin A. Hubbe, (919) 513-3022, hubbe@ncsu.edu; Lucian A. Lucia, (919) 515-7707, lucian.lucia@gmail.com URLs: bioresourcesjournal.com; http://ncsu.edu/bioresources ISSN: 1930-2126