Zhenhua Gao, Dieying Ma, Xinjing Lv, Qingwen Wang


The effects of moulding pressure and initiator content on the performances of kraft fibre-reinforced UPE composites were investigated by means of tensile evaluation, DMA analysis, SEM analysis, and short-term creep tests. The results indicated that the prepared composites had much higher tensile strength and modulus and better creep resistance than traditional thermoplastic wood plastic composites (WPCs). These improved properties resulted from the incorporation of the strong kraft fibres as reinforcement. The combination of the fibers with the thermosetting UPE matrix produced enhanced kraft-UPE interfacial adhesion. Changes in moulding pressure and initiator level produced various effects in the properties of composites. As the moulding pressure increased from 6 MPa to 25 MPa, the mechanical properties and creep resistances increased gradually until a moulding pressure of 20 MPa was reached; after this point, the values decreased. With an increase in the initiator content from 0.3 PHR (parts per hundred parts of resin) to 1.0 PHR, the tensile strength and interface adhesion first increased, then decreased, while the instantaneous strain and maximum strain values (measured in the creep tests) decreased gradually.


Wood-plastic composites; Kraft fibre; Unsaturated polyester; Molding pressure; Initiator level; Mechanical properties

Full Text:


Welcome to BioResources! This online, peer-reviewed journal is devoted to the science and engineering of biomaterials and chemicals from lignocellulosic sources for new end uses and new capabilities. The editors of BioResources would be very happy to assist you during the process of submitting or reviewing articles. Please note that logging in is required in order to submit or review articles. Martin A. Hubbe, (919) 513-3022,; Lucian A. Lucia, (919) 515-7707, URLs:; ISSN: 1930-2126