High Molecular-Weight Thermoplastic Polymerization of Kraft Lignin Macromers with Diisocyanate

Le Dai Duong, Gi-Yong Nam, Joon-Suk Oh, In-Kyung Park, Nguyen Dang Luong, Ho-Kyu Yoon, Seong-Hoon Lee, Youngkwan Lee, Ju-Ho Yun, Chong-Gu Lee, Suk-Ho Hwang, Jae-Do Nam


A high molecular-weight thermoplastic lignin-based polymer was successfully synthesized by adjusting the degree of polymerization while inducing linear growth of lignin macromers via methylene diphenyldiisocyanate. The thermoplastic lignin-urethane polymer was desirably achieved in a narrow range of reaction conditions of 2.5 to 3.5 h at 80 oC in this study, and the molecular weight of the resulting lignin-based polyurethanes (LigPU) reached as high as 912,000 g/mole, which is far above any reported values of lignin-based polymer derivatives. The thermal stability of LigPU was greatly improved by the urethane polymerization, giving the initial degradation temperature (T2%) at 204 °C, which should be compared with T2% = 104 °C of the pristine lignin. This was due to the fact that the OH groups in the lignin macromers, having low bond-dissociation energy, were replaced by the urethane bonds. In dielectric analysis, the synthesized LigPU exhibited a softening transition at 175 °C corresponding to a combinatorial dual process of the dry Tg,dry of the lignin macromers and the softening of methylenediphenyl urethane chains. This work clearly demonstrated that a high molecular weight of thermoplastic LigPU could be desirably synthesized, broadening the lignin application for value added and eco-friendly products through common melt processes of polymer blend or composites.


Lignin;Lignin-based polyurethane; Eco-friendly; Dielectric analysis; Glass transition temperature

Full Text:


Welcome to BioResources! This online, peer-reviewed journal is devoted to the science and engineering of biomaterials and chemicals from lignocellulosic sources for new end uses and new capabilities. The editors of BioResources would be very happy to assist you during the process of submitting or reviewing articles. Please note that logging in is required in order to submit or review articles. Martin A. Hubbe, (919) 513-3022, hubbe@ncsu.edu; Lucian A. Lucia, (919) 515-7707, lucian.lucia@gmail.com URLs: bioresourcesjournal.com; http://ncsu.edu/bioresources ISSN: 1930-2126