Tensile Properties of Bamboo Fiber-reinforced Polypropylene Composites Modified by Impregnation with Calcium Carbonate Nanoparticles

Cuicui Wang, Yu Xian, Haitao Cheng, Wenyan Li, Shuangbao Zhang


Tensile properties of bamboo fiber (BF)/polypropylene (PP) composites were investigated for different impregnation modification processes. The surface morphology of BF and the fracture morphology of the BF/PP composites were examined by scanning electron microscopy (SEM). Images showed that CaCO3 nanoparticles (nano-CaCO3) adhered to the fiber surfaces. Tension tests of individual bamboo fibers (IBFs) and the BF/PP composites were conducted. The results indicated that the tensile strength (TS), modulus of elasticity (MOE), and elongation at break (EAB) of IBFs increased by 16.0%, 22.2%, and 5.2%, respectively, while those of the BF/PP composites increased by 3.0%, 7.0%, and 15.8%, respectively, compared to the control samples. Various process parameters during the impregnation with nano-CaCO3 had marked effects on the tensile properties of the composites. The optimal conditions for BF-reinforced PP composites by impregnation modification were determined to be a nano-CaCO3 concentration of 1.0×10-2 g/mL, an ethylenediamine tetraacetic acid disodium salt (EDTA-2Na) additive concentration of 8.5×10-4 g/mL, and an impregnation time of 25 min.


Calcium carbonate nanoparticles (nano-CaCO3); Polypropylene (PP); Bamboo fiber (BF); Composites; Tensile properties

Full Text:


Welcome to BioResources! This online, peer-reviewed journal is devoted to the science and engineering of biomaterials and chemicals from lignocellulosic sources for new end uses and new capabilities. The editors of BioResources would be very happy to assist you during the process of submitting or reviewing articles. Please note that logging in is required in order to submit or review articles. Martin A. Hubbe, (919) 513-3022, hubbe@ncsu.edu; Lucian A. Lucia, (919) 515-7707, lucia-bioresources@ncsu.edu URLs: bioresourcesjournal.com; http://ncsu.edu/bioresources ISSN: 1930-2126