Preparation and Surface Sizing Application of Sizing Agent Based on Collagen from Leather Waste

Xuechuan Wang, Yuemei Shang, Longfang Ren, Sufeng Zhang, Peiying Guo


Collagen extracted from leather waste was modified with maleic anhydride. Then, using ammonium persulfate as an initiator, by pre-modifying collagen reacted with styrene and ethyl acrylate monomers, a vinyl-grafted collagen sizing agent (VGCSA) for paper was prepared. Before the experiment, the performance of VGCSA was tested and VGCSA emulsion was applied to the surface sizing of the corrugated paper. Effects of the amount of VGCSA, the compound proportion of VGCSA, and starch and styrene-acrylic emulsion were studied relative to paper properties. The morphological changes of the paper before and after sizing were characterized by SEM. It was found that the collagen reacted with styrene and ethyl acrylate monomers. Through the grafting of vinyl and collagen, the crystallinity and thermal stability of VGCSA increased. The structure of VGCSA was spherical with a uniform size, and the average particle size was approximately 350 to 400 nm. After being sized, the surface fibers of paper became smooth and orderly. The optimal sizing of VGCSA was 8 g/m2. The optimal proportion of VGCSA with starch was 4:6, and the optimal proportion of VGCSA with SAE was 2:8. The research indicates that collagen extracted from leather waste could be used as a biomaterial, and environmental and economic benefits could be created as well.


Waste leather collagen; Vinyl modification; Paper sizing agent; Applications

Full Text:


Welcome to BioResources! This online, peer-reviewed journal is devoted to the science and engineering of biomaterials and chemicals from lignocellulosic sources for new end uses and new capabilities. The editors of BioResources would be very happy to assist you during the process of submitting or reviewing articles. Please note that logging in is required in order to submit or review articles. Martin A. Hubbe, (919) 513-3022,; Lucian A. Lucia, (919) 515-7707, URLs:; ISSN: 1930-2126