Manufacturing Technology and Parameter Optimization for Composite Board from Corn Stalk Rinds

Xun He, Defu Wang, Yanling Zhang, Yong Tang


To improve the bonding strength between adhesive and enhance the performance of composite board made from corn stalk rinds, a method for preparing three-layer composite boards was proposed. Accordingly, corn stalk rinds with the epidermis removed, were used as the core layer, while crushed aggregates from the epidermis were used as the surface layer of the composite board. Single-factor and orthogonal experiments were conducted to analyze the effects of the sampling height of corn stalk rinds, the surface layer proportions, and the hot-pressing temperature and time on the physico-mechanical properties of composite board. The resulting composite board from corn stalk rinds showed enhanced properties, except for the internal bond strength (P < 0.01). The physical properties of the composite board were significantly improved (P < 0.01) by removing the crushed aggregates of the epidermis, forming a single layer of composite board. The optimal parameters were as follows: the sampling height below the ear part of the corn stalk rinds; 12% surface layers; 150 °C hot-pressing temperature; and 6 min time. Under these conditions, the physico-mechanical properties of the composite board met the requirement level for particleboard. This research supports the use of corn stalk rinds as composite boards.


Corn stalk rind; Epidermis; Three-layer composite board; Manufacturing technology

Full Text:


Welcome to BioResources! This online, peer-reviewed journal is devoted to the science and engineering of biomaterials and chemicals from lignocellulosic sources for new end uses and new capabilities. The editors of BioResources would be very happy to assist you during the process of submitting or reviewing articles. Please note that logging in is required in order to submit or review articles. Martin A. Hubbe, (919) 513-3022,; Lucian A. Lucia, (919) 515-7707, URLs:; ISSN: 1930-2126