Effect of Infill Value on Decay Resistance, Thermal, and Mechanical Properties of 3D Printed Polylactic Acid Composites Filled with Wood Fibers

Yufeng Sun, Danbee Lee, Yapeng Wang, Suiliang Li, Jilai Ying, Xinping Liu, Guangyin Xu, Jaegyoung Gwon, Qinglin Wu

Abstract


Polylactic acid (PLA)-based composites with wood filler were 3D-printed using fused deposition modeling (FDM) at different infill settings (i.e., 10 to 100%) to evaluate their strength and biodegradation properties. Microvoids were present in the commercial wood-filled PLA filaments. Wood-PLA filament had reduced thermal stability compared with mineral-filled PLA filament due to the presence of thermally degradable wood flour. The printed composites had a denser internal structure with increased infill. The flexural modulus of elasticity and modulus of rupture also increased with infill value. Sixteen-week fungi test performed using a brown rot, Postia placenta, and a white rot, Irpex lacteus, did not lead to significant sample weight loss and strength reduction for composites at various infill values. Therefore, 3D printed composites with PLA-based filament containing 30 wt.% wood fiber were shown to be resistant to biodegradation by common decay fungi.

Keywords


Wood-filled PLA; 3D printing; Infill rate; White rot; Brown rot

Full Text:

PDF


Welcome to BioResources! This online, peer-reviewed journal is devoted to the science and engineering of biomaterials and chemicals from lignocellulosic sources for new end uses and new capabilities. The editors of BioResources would be very happy to assist you during the process of submitting or reviewing articles. Please note that logging in is required in order to submit or review articles. Martin A. Hubbe, (919) 513-3022, hubbe@ncsu.edu; Lucian A. Lucia, (919) 515-7707, lucia-bioresources@ncsu.edu URLs: bioresourcesjournal.com; http://ncsu.edu/bioresources ISSN: 1930-2126